Heat resistance of graphitized steel

V. O. Savchenko

Abstract


Purpose. The investigation of temperature dependences of steels' mechanical properties and heat resistance under conditions of thermal cyclic loads. It's necessary to determine the mechanical properties and heat resistance indices of graphitized steels and cast iron VCh400 within the temperature range of 20…800°С. Methodology. Graphitized steels of the following chemical composition (mass %): 0.61…1.04C; 1.19…1.59%Si; 0.32…0.37%Mn; 0.12…0.17%Al; 0.008…0.014%S and 0.016…0.025%Р have been heat-treated according to the mode: heating up to 810°С – holding for 2 hours; cooling down to 680°С – holding for 2 hours with further cooling using the furnace in order to provide the ferrite-pearlite metallic base with graphite inclusions. In order to determine heat resistance indices (heat stresses index K and the material's resistance criterion at thermal cyclic load C) the indices of graphitized steels' and cast irons' mechanical properties in the temperature range of 20…800°С have been investigated. Findings. It has been established that as a result of lower carbon content and smaller quantity of graphite inclusions, graphitized steel exceeds such indices of nodular cast iron VCh400 as: tensile strength and plasticity at room and high temperatures, and also heat resistance criteria K and C. This steel can be used to manufacture articles operating under conditions of thermal cyclic loads. Originality. Tensile strength and percent elongation of graphitized steels within the temperature range of 20…800°С have been determined. Calculations of heat resistance criteria to the heat stresses index K and the material's resistance criterion at thermal cyclic loads C within the temperature range 20…800°С in comparison with nodular cast iron of VCh400 grade have been carried out. Practical value. The expediency of using graphitized steel for manufacturing of articles operating under conditions of thermal cyclic loads has been shown.


Keywords


graphitized steel; mechanical properties; heat resistance; thermal cyclic loads

References


Abramov V.V., Kurganov V.A. Termouravnoveshennaya izlozhnitsa [Thermally balanced ingot mould].Moscow, Metallurgiya Publ., 1972. 144 p.

Akimov I.V. Povysheniye iznosostoykosti grafityzovannykh staley [Increasing of wear resistance of the graphitized steels]. Visnyk Dnipropetrovskoho natsionalnoho universytetu zaliznychnoho transportu imeni akademika V. Lazariana [Bulletin of Dnipropetrovsk National University of Railway Transport named after Academician V. Lazaryan], 2013. issue 48, pp. 81-87.

Vakulenko І.О., Anofriiev V.H. Metalevi materialy z pidvishchenoiu mitsnistiu dlia vyhotovlennia vahoniv [Metallic materials with increased strength for cars manufacture]. Visnyk Dnipropetrovskoho natsionalnoho universytetu zaliznychnoho transportu imeni akademika V. Lazariana [Bulletin of Dnipropetrovsk National University of Railway Transport named after Academician V. Lazaryan], 2011, issue 37, pp. 216-219.

Volchok I.P., Yakovlev A.Yu. Optimizatsiya sostava termostoykoy grafitizirovannoy stali [Optimization of heat resistant graphitized steel composition]. Stroitelstvo, materialovedeniye, mashinostroeniye [Consruction, material science, mechanic engineering], Dnipropetrovsk, 2007, issue 41, part 1, pp. 119-125.

Voronova N.A., Geld V.P., Tkach N.T. Otlivka izlozhnits iz magniyevogo chuguna [Casting of ingot moulds from magnesium cast iron]. Povysheniye stoykosti izlozhnits. Tematicheskiy otraslevoy sbornik № 1 [Increasing of ingot moulds' strength. Thematic and specialized proc. no. 1],Moscow, 1972, pp. 75-87.

Gubkin S.I. Deformiruyemost metallov [Deformability of metals]. Moscow, Metallurgizdat Publ., 1953. 350 p.

Dodin Ya.L., Saksonov L.G., Sokolovskiy L.O., Torbochkin L.I. Izlozhnitsy dlya slitkov legirovannykh staley [Ingot moulds for ingots of alloyed steels].Moscow, Metallurgizdat Publ., 1963. 192 p.

Sanin F.P., Kuchma L.D., Dzhur Ye.O., Sanin A.F. Tverdopalyvni raketni dvyhuny. Materialy i tekhnolohii [Solid-fuel rocket engines. Materials and technologies]. Donetsk, Vydavnytstvo DDU Publ., 1999. 318 p.

Okhotin A.S. Teploprovodnost tverdykh tel [Heat conductivity of solid bodies].Moscow, Energoizdat Publ., 1984. 321 p.

Neimark B.E. Fizicheskiye svoystva staley i splavov, primenyayemykh v energetike. [Physical properties of steels and alloys used in energetics]. Moscow-Leningrad, Energiya Publ., 1967. 240 p.

VolchokI.,AkimovI., SavchenkoV. Heat resistance of graphitized steel. Problems of modern Techniques in Engineering and Education-2009.Krakow, 2009, pp. 103-107.

Kawabata Yoshikazu, Morita Masahiko, Togashi Fusao. Graphite Precipitated hot-rolled Steel plate having workability and hardenability and method therefore. PatentUSA, no. US19920822649, 1992.

Katayama Sakae, Tarui Toshimi, Toda Masahiro, Naito Ken-Ichiro. Fine Graphite uniform dispersion steel excellent in gold Machinability, Cuttability and Hardenbility, and production method for the same. PatentJapan, no. US19960700355, 1996.


GOST Style Citations


Абрамов, В. В. Термоуравновешенная изложница / В. В. Абрамов, В. А. Курганов. – М. : Металлургия, 1988. – 144 с.

Акимов, И. В. Повышение износостойкости графитизированных сталей / И. В. Акимов // Наука та прогрес трансп. Вісн. Дніпропетр. нац. ун-ту залізн. трансп. – 2013. – № 6 (48) – С. 81−87.

Вакуленко, І. О. Металеві матеріали з підвищеною міцністю для виготовлення вагонів / І. О. Вакуленко, В. Г. Анофрієв // Вісн. Дніпропетр. нац. ун-ту залізн. трансп. ім. акад. В. Лазаряна. – Д., 2011. – Вип. 37. – С. 216−219.

Волчок, И. П. Оптимизация состава термостойкой графитизированной стали / И. П. Волчок, А. Ю. Яковлев // Стр-во, материаловедение, машиностроение : сб. научн. тр. под ред. В. И. Большакова. – Вып. 41. Часть 1. – Д. : ПГАСА, 2007. – С. 119−125.
Воронова, Н. А. Отливка изложниц из магниевого чугуна / Н. А. Воронова, В. П. Гельд, Н. Т. Ткач // Повышение стойкости изложниц. Темат. отраслевой сб. № 1. – М. : Металлургия, 1972. – С. 75−87.

Губкин, С. И. Деформируемость металлов / С. И. Губкин. – М. : Металлургиздат, 1953. – 350 с.

Изложницы для слитков легированных сталей / Я. Л. Додин, Л. Г. Саксонов, Л. О. Соколовский, Л. И. Торбочкин. – М. : Металлургиздат, 1963. − 192 с.

Твердопаливні ракетні двигуни. Матеріали і технології / Ф. П. Санін, Л. Д. Кучма, Є. О. Джур, А. Ф. Санін. – Д. : Вид-во ДДУ, 1999. − 318 с.

Теплопроводность твердых тел : справ. / под ред. А. С. Охотина. – М. : Энергоиздат, 1984. – 321 с.

Физические свойства сталей и сплавов, применяемых в энергетике : справ. / под ред. Б. Е. Неймарка. − М.−Л. : Энергия, 1967. – 240 с.

Volchok, I. Heat resistance of graphitized steel / Ivan Volchok, Ivan Akimov, Vera Savchenko // Problems of modern Techniques in Engineering and Education-2009. − Krakow: Zaklad Uslug Poligroficznych, 2009. – Р. 103–107.

Pat. 5,139,583, C22C38/00. Graphite Precipitated hot-rolled Steel plate having workability and hardenability and method therefore / Yoshikazu Kawabata, Masahiko Morita, Fusao Togashi (USA). – № US19920822649 ; filed. 21.01.92 ; publ. 18.08.92.

Pat. US5830285, C21D1/26; C21D1/84, C21D8/06, C22C38/12, C22C38/60. Fine Graphite uniform dispersion steel excellent in gold Machinability, Cuttability and Hardenbility, and production method for the same / Sakae Katayama, Toshimi Tarui, Masahiro Toda, Ken-Ichiro Naito (Japan). – № US19960700355 ; filed. 23.08.96 ; publ. 03.11.98.



DOI: https://doi.org/10.15802/stp2014/27333

 

Cited-by:

1. INCREASING OF MECHANICAL PROPERTIES OF CAST GRAPHITIZED STEEL
I. V. Akimov
Science and Transport Progress. Bulletin of Dnipropetrovsk National University of Railway Transport  Issue: 3(57)  First page: 129  Year: 2015  
doi: 10.15802/stp2015/46071



Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.

 

ISSN 2307–3489 (Print)
ІSSN 2307–6666 (Online)